Stannol Wire, 1mm Lead solder, 296°C Melting Point

RS Stock No.: 517-968Brand: StannolManufacturers Part No.: 631261
brand-logo
View all in Home

Technical documents

Specifications

Brand

Stannol

Wire Diameter

1mm

Model Number

HS10

Percent Lead

93%

Product Form

Wire

Melting Point

296°C

Percent Silver

2%

Percent Tin

5%

Flux Type

Rosin Based

Product Weight

500g

Flux Content Percent

2.5%

Country of Origin

Germany

Product details

Soldering wire HS10, Pb93Sn5Ag2

Tin-lead-silver soldering alloy with 2.5% colophony flux core
Pb93Sn5Ag2 solder with high melting point
Particularly suitable for use on products subject to high temperatures such as ovens and engines
The silver content of the solder provides stability and cross-linking strength to the soldered joint, therefore preventing embrittlement even under extreme atmospheric conditions
Solidus at 296 °C, liquidus at 301 °C

Standards

EN ISO 9453:2006

You may be interested in

Stock information temporarily unavailable.

Please check again later.

Stock information temporarily unavailable.

P.O.A.

Stannol Wire, 1mm Lead solder, 296°C Melting Point

P.O.A.

Stannol Wire, 1mm Lead solder, 296°C Melting Point
Stock information temporarily unavailable.
You may be interested in

Technical documents

Specifications

Brand

Stannol

Wire Diameter

1mm

Model Number

HS10

Percent Lead

93%

Product Form

Wire

Melting Point

296°C

Percent Silver

2%

Percent Tin

5%

Flux Type

Rosin Based

Product Weight

500g

Flux Content Percent

2.5%

Country of Origin

Germany

Product details

Soldering wire HS10, Pb93Sn5Ag2

Tin-lead-silver soldering alloy with 2.5% colophony flux core
Pb93Sn5Ag2 solder with high melting point
Particularly suitable for use on products subject to high temperatures such as ovens and engines
The silver content of the solder provides stability and cross-linking strength to the soldered joint, therefore preventing embrittlement even under extreme atmospheric conditions
Solidus at 296 °C, liquidus at 301 °C